PU sealant for autoglass repaired bonding or sealing CAS NO.9009-54-5
- Min.Order: 100 Kilogram
- Payment Terms: T/T
- Product Details
Keywords
- Polyurethane sealant
- autoglass
- auto glass repaired
Quick Details
- ProName: PU sealant for autoglass repaired bond...
- CasNo: 9009-54-5
- Appearance: black paste
- Application: After repaired auto glass, you need to...
- DeliveryTime: 1DAY
- PackAge: 310ml/aluminum tube, 40 cartridges in ...
- Port: TIANJIN QINGDAO SHANGHAI
- ProductionCapacity: 2 Metric Ton/Day
- Purity: 10%
- Storage: Store in cold cool, dry place, below25...
- Transportation: normal delivery conditions
- LimitNum: 100 Kilogram
- Operating Temperature: -50℃ and 100℃
- Valid Period: 45mins
- Shear Strength: 3.0min
- Curing Time: 7days
Superiority
M-103/103A polyurethane sealant for auto glass repaired is a single -component, moisture curable at room temperature with normal adhesive strength in paste form, Non-toxic, odorless. None-solvent, none-corrosion and no pollution to the environment. After solidified to be rubber form, it has a good elasticity and performs stable between -50℃ and 100℃. low VOC,low odor, middle adhesive strength,easy handling.
Details
Puyang wanquan chemical company is the leading producer of PU sealant in china, we start to produce since 1994.
M-103/103A PU sealant mainly used for auto glass repaired,or some vehicles glass need middle or low strength bonding or sealing, M-103/103A will be your best choice for this, good price with good quality, for those glass sealing, you can choose this.
M-103 PU sealant mainly specifications as below:
| Color | Black paste |
| Surface drying time(min) | 40±5 |
| Curing rate(mm/24h) | ≥3 |
| Density(g/ml) | 1.2±0.1 |
| Sag(mm) | ≤0 |
| Hardness | 45±5 |
| Elongation(%) | ≥300 |
| Tensile strength(mpa) | ≥5.0 |
| Shearing strength(mpa) | ≥3.0 |
| Tearing strength(n/mm) | ≥20.0 |
M-103A specifications as below:
| Color | Black paste |
| Surface drying time(min) | 30±5 |
| Curing rate(mm/24h) | ≥3 |
| Density(g/ml) | 1.2±0.1 |
| Sag(mm) | ≤0 |
| Hardness | 50±5 |
| Elongation(%) | ≥300 |
| Tensile strength(mpa) | ≥4.0 |
| Shearing strength(mpa) | ≥2.5 |
| Tearing strength(n/mm) | ≥18 |